English: Typical macrostructure of a cast ingot. The chill zone is on the outside, against the mold walls, then the columnar zone protruding from the chill zone to the equiaxed zone, and finally the equiaxed zone in the middle. For materials with wide solidification temperatures the top is concave due to shrinkage (as shown), but for materials with a narrow solidification temperature range the shrinkage takes the form of a pipe in the center of the ingot. The mold usually has a draft to ease the removal of the casting. Français : Morphologie cristalline typique d'un lingot : structure colonnaire à l'extérieur, puis structure dendritique, et structure équiaxe au cœur, avec une retassure sur le dessus — le profil du moule est normalement trapézoïdal, afin de pouvoir démouler le lingot |
| Tanggal | (UTC) |
| Sumber | |
| Pembuat |
|
Saya, pemilik hak cipta dari karya ini, dengan ini menerbitkan berkas ini di bawah ketentuan berikut:
  
|
Berkas on ipartandoan sian on Creative Commons Attribution-Share Alike 3.0 Unported partadoan. | |
| ||
| Label lisensi ini ditambahkan pada berkas sebagai bagian dari pemutakhiran lisensi GFDL. |
|
Diizinkan untuk menyalin, mendistribusikan dan/atau memodifikasi dokumen ini di bawah syarat-syarat Lisensi Dokumentasi Bebas GNU, Versi 1.2 atau lebih baru yang diterbitkan oleh Free Software Foundation; tanpa Bagian Invarian, tanpa Teks Sampul Depan, dan tanpa Teks Sampul Belakang. Salinan lisensi dimasukkan ke bagian yang berjudul Lisensi Dokumentasi Bebas GNU. |
Anda dapat memilih lisensi pilihan Anda.
Log pengunggahan asli
This image is a derivative work of the following images:
- File:Structure_cristalline_lingot.svg licensed with Cc-by-sa-3.0-migrated, GFDL
- 2007-02-20T09:48:26Z Cdang 312x191 (45908 Bytes) {{Information |Description={{en|Typical crystalline structure of an ingot: columnar structure on the exterior side, then dendrites, and equiaxial structure in the core, and a depression on the top}} {{fr|Structure cristalline
Uploaded with derivativeFX
Riwayat berkas
Klik pada tanggal/waktu untuk melihat berkas ini pada saat tersebut.
| Tanggal/Waktu | Miniatur | Dimensi | Pengguna | Komentar | |
|---|---|---|---|---|---|
| terkini | 11 Juni 2022 21.49 | | 350 × 175 (44 KB) | EllieBellie25 | File uploaded using svgtranslate tool (https://svgtranslate.toolforge.org/). Added translation for nl. |
| 2 Oktober 2009 22.55 |  | 350 × 175 (45 KB) | Wizard191 | {{Information |Description={{en|Typical macrostructure of a cast ingot. The chill zone is on the outside, against the mold walls, then the columnar zone protruding from the chill zone to the equiaxed zone, and finally the equiaxed zone in the middle. For |
Penggunaan berkas
Halaman berikut menggunakan berkas ini:
Penggunaan berkas global
Wiki lain berikut menggunakan berkas ini:
- Penggunaan pada ca.wikipedia.org
- Penggunaan pada de.wikipedia.org
- Penggunaan pada en.wikipedia.org
- Penggunaan pada fa.wikipedia.org
- Penggunaan pada ja.wikipedia.org
- Penggunaan pada nl.wikipedia.org
- Penggunaan pada no.wikipedia.org